Structural characterization of the Ta5Si3 and Cr5Si3 phases

Autores

  • Lívia Ribeiro Universidade de São Paulo
  • Sergio Renosto Universidade de São Paulo
  • Paulo Atsushi Suzuki Universidade de São Paulo

Resumo

In recent studies, much research is focused on the silicides alloys based in refractory transitions metal, becoming these materials as potential candidate for structural applications in high-temperatures for the fact of them possess excellent balance of properties, of is extreme importance for aeronautical and aerospace industries. This work presents results of microstructural characterization of the Ta5Si3 and Cr5Si3 important phases. These silicides were obtained by arc melting under argon atmosphere. Analyzes generated by X-ray Diffraction (XRD) and Scanning Electron Microscope (SEM) were used to obtain information about chemical and crystallographic characteristics of the samples generated before and after the heat-treatment

Downloads

Publicado

2009-04-08

Edição

v. 13 n. 2 (2007)

Seção

Artigos

Licença

A submissão de originais para este periódico implica na transferência, pelos autores, dos direitos de publicação impressa e digital. Os direitos autorais para os artigos publicados são do autor, com direitos do periódico sobre a primeira publicação. Os autores somente poderão utilizar os mesmos resultados em outras publicações indicando claramente este periódico como o meio da publicação original.