Reuse of glass cullet as aggregate for red ceramic clays

Autores

  • Silvio Rainho Teixeira Department of Physics, Chemistry and Biology, São Paulo State University (UNESP)
  • Francine Bettio Costa Department of Physics, Chemistry and Biology, São Paulo State University (UNESP)
  • Agda Eunice de Souza Department of Physics, Chemistry and Biology, São Paulo State University (UNESP)
  • Gleyson Tadeu Almeida Santos Department of Physics, Chemistry and Biology, São Paulo State University (UNESP)

Resumo

Numerous silicates based wastes have been produced and considered for recycling and reuse. Among them, glass cullet is one of the most common silicate wastes and has considerable volume in the cities wastes. A big amount of this waste is recycled by the glass industry but another part is dumped in the cities garbage deposits. In the last few decades there has been considerable research on the reuse of glass waste as aggregate to produce glass-ceramic, for mortars, ceramics and for cement and concrete. This work is concerned to study the reuse of one way glass bottles as aggregate to produce bricks and roof tales (red ceramic). Two kinds of glass powder were prepared by sieving (0.037 to 0.088 mm and 0.088 to 0.125 mm). Prismatic ceramic bodies (CB) were pressed (60 x 20 x ~5 mm) using a ceramic mass with 0, 5, 8 and 10 % of glass cullet powder added and fired at Five different temperatures (800 to 1200 oC). The results of the technological tests (flexural strength, water absorption, dimensional changes, density and porosity apparent) show that shrinkage increases with the glass content and all other properties above are improved. These changes are more exhibited at temperatures higher than 900°C and in the higher powder glass concentrations (8 e 10%).

Downloads

Edição

Seção

Artigos