USE OF INDUSTRIAL SLAG AS AN ECOLOGICAL ALTERNATIVE IN SAW WELDING
DOI:
https://doi.org/10.69609/1516-2893.2025.v31.n2.a4058Keywords:
Soldagem por arco submerso, Escória reciclada, Sustentabilidade, Aço ASTM A36, Reaproveitamento de resíduos industriaisAbstract
This study aims to evaluate the technical and environmental feasibility of reusing slag from the submerged arc welding (SAW) process, aiming at reducing industrial waste and developing sustainable practices. The base material used was ASTM A36 steel, widely used in structural applications. Three experimental conditions were performed: CP1 (100% fresh active flux), CP2 (50% fresh flux and 50% ground slag), and CP3 (100% ground slag). The tests included visual inspection, liquid penetrant testing, macrographic analysis, particle size distribution, and Rockwell A hardness. The results indicated that none of the samples presented critical discontinuities, maintaining good surface integrity. Sample CP2 obtained the highest penetration (15.55 mm), while CP3 presented the lowest (11.43 mm), demonstrating that partial slag replacement does not compromise metallurgical performance. Dilution ranged from 51% to 55%, with negligible differences between the compositions. The granulometric analysis revealed a predominant concentration between the 20/40 meshes, the fines content increased with the use of recycled slag. The average hardness varied by less than 1 HRA between conditions, making it statistically insignificant. Therefore, it can be concluded that replacing up to 50% of the new flux with recycled slag is technically feasible, maintaining the metallurgical properties of the weld bead. This proposal contributes to sustainability in welding, reducing costs and the environmental impact associated with the disposal of industrial solid waste, without compromising process quality.
Downloads
Metrics
References
BATISTA, D. S.; SANTANA, J.L. A influência da granulometria do fluxo ativo no Processo de Soldagem Arco submerso “SAW” no aço ASTM A36. 2022. 49p. Trabalho de Graduação (Curso de Mecânica em Processos de Soldagem). Faculdade de Tecnologia de Pindamonhangaba. Pindamonhangaba. 2022.
BENEVIDES, K. D. G.; BENEVIDES, P. P.; BENEVIDES , M. P.; VIAGI, A. F.; MOURA, R. A. (2025). Neuroengenharia: uma pesquisa sobre Inteligência Artificial em um posto de trabalho compartilhado entre humano e máquina. Revista Exatas, [S. l.], v31, n2, 2025. DOI: 10.69609/1516-2893.2025.v31.n2.a4017. https://periodicos.unitau.br/exatas/article/view/4017
CASTRO, J. N.; PINHEIRO, B. R; M. M. F., Estudo da Variação da DBCP e do ângulo de soldagem em corrente pulsada, curto-circuito convencional e curto-circuito controlado em soldagem MIG/MAG 72º Congresso Anual da ABM, Internacional e ao 17º ENEMET - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas, parte integrante da ABM Week, realizada de 02 a 06 de outubro de 2017, São Paulo, SP, Brasil.
COSTA, M. S. W. Caracterização das Escórias Geradas no Processo de Soldagem ao Arco Submerso e suas vias de Reutilização. 2018. 59p. Trabalho de Conclusão de Curso apresentado no Curso de Graduação em Engenharia de Materiais do Centro Federal de Educação Tecnológica de Minas Gerais. Belo Horizonte - Minas Gerais. 2018.
CUNHA, I. O. J.; JUNIOR, I. A. C.; MOURA, G. G.; MOURA, R. A.; SILVA, M. B. Segurança e ergonomia para força laboral feminina: interação com máquinas colaborativas. Sodebras. Vol. 16. N° 187. 2021. ISSN 1809-3957. DOI: https://doi.org/10.29367/issn.1809-3957.16.2021.187.08
DA SILVA FILHO, A. L.; BENEVIDES, M. P.; NOHARA, E. L.; DE MOURA, R. A. (2025). Engenharia mecânica na construção de máquina-ferramenta portátil para usinar peças de até 1200 milímetros de diâmetro. ARACÊ , [S. l.], v. 7, n. 7, p. 40298–40314, 2025. DOI: 10.56238/arev7n7-295. https://periodicos.newsciencepubl.com/arace/article/view/6788
FELIZARDO, I. Apostila - Tecnologia da Soldagem. 2016. 113p. Departamento de Engenharia Mecânica. Centro Federal de Educação Tecnológica de Minas Gerais - CEFET-MG. 2016.
MARÇAL, I.S.L.; SPOLZINO, L.E.C.L.; Estudo do Processo de Soldagem por MIG em Material A-36 com Adição de Óxido de Titânio. 2022. 46p. Trabalho de Graduação (Curso de Mecânica em Processos de Soldagem). Faculdade de Tecnologia de Pindamonhangaba/SP. 2022.
MOURA, R. A.; MARÍLIO, J. W. O.; MARQUES, D. J. R.; OLIVEIRA, M. R.; SILVA, M. B. (2024). Neuroergonomia aplicada na engenharia para testar materiais mais leves e confortáveis para usuários de cadeiras de rodas. Revista SODEBRAS, Vol. 19, N° 221, 2024. DOI: https://doi.org/10.29367/5bge8b53 . https://revista.sodebras.com.br/index.php/revista/article/view/13/8
NAZARÉ, V. D. M. Estudo da Pronfundidae e Diluição do Aço A36 com a Variação da Inlinação do Ângulo da Tocha No Processo MIG (GMAW). 2022. 42p. Trabalho de Graduação (Curso de Tecnologia em Processos Metalúrgicos). Faculdade de Tecnologia de Pindamonhangaba. Pindamonhangaba.-SP 2022.
OLIVEIRA, M. R.; BENEVIDES, K. G.; RUFINO, L. G. C.; SANTOS, D. A.; BENEVIDES, M. P.; MOURA, R. A. (2025). Direito Digital e sua limitação no uso da inteligência artificial hodierna: um ponto para reflexão e ações requeridas. DOI: 10.55905/revconv.18n.7-341. Disponível em: https://ojs.revistacontribuciones.com/ojs/index.php/clcs/article/view/19679
ROMÃO, E. J. E.; SILVA, L. F. N. Análise do Perfil de Dureza da Solda, Variando a Temperatura de Pré-Aquecimento. 2018. Trabalho de Graduação (Curso de Tecnologia em Processos Metalúrgicos). Faculdade de Tecnologia de Pindamonhangaba. 2018.
SANTOS, C.E.F Processo de Soldagem Conceitos, Equipamentos e Normas de Segurança Érica, 152p São Paulo 2015.
SILVA, L. G. C. Estudo dos Efeitos da Adição de Óxido de Titânio na Soldagem por Arco Submerso. 2023. 53p. Trabalho de Graduação do Curso de Tecnologia em Processos Metalúrgicos. Faculdade de Tecnologia de Pindamonhangaba. Pindamonhangaba/SP. 2023.
SILVA, R. C.; GHENO, S. M. Caracterização Mecânica e Estrutural do Aço Astm A131 Classe DH36 em Comparação com Aço ASTM A36 Utilizado para Projetos Estruturais. I STEFA Simpósio de Tecnologia Fatec Sertãozinho. 2018. Fatec Sertãozinho-São Paulo.
SOUZA NETO, E.C., Avalição da Resistência ao Desgaste de Revestimentos Duros Aplicados por Soldagem em Martelo Triturados de Baterias Automotivas. Dissertação mestrado em Eng. Mecânica, Universidade Federal de Campina Grande, Centro de Ciência e tecnologia, 2015.
SOUZA, L. Influência do Preaquecimento e do Sentido de Soldagem no Processo TIG Sobre a Microestrutura e as Propriedades Mecânicas do Aço ABNT 1020. 2021. 59p. Trabalho de Conclusão de Curso apresentado ao Curso Superior de Tecnologia em Fabricação Mecânica do Campus Jaraguá do Sul, do Instituto Federal de Santa Catarina, Jaraguá do Sul/SC. 2021.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2025 Paulo Sérgio da Silvia , Agnaldo Benedito Moreira , Edilon de Oliveira França
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.
A submissão de originais para este periódico implica na transferência, pelos autores, dos direitos de publicação impressa e digital. Os direitos autorais para os artigos publicados são do autor, com direitos do periódico sobre a primeira publicação. Os autores somente poderão utilizar os mesmos resultados em outras publicações indicando claramente este periódico como o meio da publicação original.
English
Español (España)
Português (Brasil)